Rheology Modifier BP-183-A13
BP-183-A13 belongs to the unconventional type of organoclays group, being an easy-to-disperse, self-activated Rheology Modifier.
1. Advantages:
☆High gelling efficiency over low,medium and high polarity organic liquids.
☆Easy of incorporation.No need for polar activator or making pregel.
☆Consistent in rheology and thixotropy development.
☆Easy of dispersion especially in styrene and alcohol solvent. Dust-free addition.
☆Good anti-sagging property and anti-sediment property.
☆Can replace fumed silica in epoxy resin systems and unsaturated resin systems with
better thixotropy performance and more economical price.
2. Typical Properties:
3. Typical Applications:
4. Incorporations:
BP-183-A13 belongs to the unconventional type of organoclays group, being an easy-to-disperse, self-activated organoclay, BP-183-A13 does not require a chemical (polar) activator to reach the proper level of delamination of the organoclay platelet stacks.
However, in systems like styrene, xylene,200#solvent oil and compound solvent, pre-gel method is also acceptable.
5. Recommended Levels:
The amount of BP-183-A13 Rheology Modifier required depends upon the type of organic system and the degree of thickening or other properties desired. Addition levels are typically between 0.2%-0.6% based on the total formulation weight. For special purpose, for example, in hand layup unsaturated resin,1-6% is recommended.
6. International Countertype: Garamite®1958
☆High gelling efficiency over low,medium and high polarity organic liquids.
☆Easy of incorporation.No need for polar activator or making pregel.
☆Consistent in rheology and thixotropy development.
☆Easy of dispersion especially in styrene and alcohol solvent. Dust-free addition.
☆Good anti-sagging property and anti-sediment property.
☆Can replace fumed silica in epoxy resin systems and unsaturated resin systems with
better thixotropy performance and more economical price.
2. Typical Properties:
| Color | Appearance | Bulk Density |
Moisture (@105℃,2hrs) |
Loss on Ignition ( @1000℃ ) |
| Pale Yellow | Free Flowing Powder | 150g/L | ≤8.0% | ≤30% |
3. Typical Applications:
| ●Anti-corrosion paint | ●Polyester paint |
| ●Industrial paint | ●Solvent epoxy paint |
| ●Non-solvent epoxy paint | ●Adhesive |
| ●Putties and sealant | ●Varnish |
4. Incorporations:
BP-183-A13 belongs to the unconventional type of organoclays group, being an easy-to-disperse, self-activated organoclay, BP-183-A13 does not require a chemical (polar) activator to reach the proper level of delamination of the organoclay platelet stacks.
However, in systems like styrene, xylene,200#solvent oil and compound solvent, pre-gel method is also acceptable.
5. Recommended Levels:
The amount of BP-183-A13 Rheology Modifier required depends upon the type of organic system and the degree of thickening or other properties desired. Addition levels are typically between 0.2%-0.6% based on the total formulation weight. For special purpose, for example, in hand layup unsaturated resin,1-6% is recommended.
6. International Countertype: Garamite®1958